该系列产品是用有机过氧化物热硫化成型的绝缘固体硅橡胶，适合生产冷缩电力电缆附件，其中TRK7141, TRK7341常用于加热模压硫化成型，TRK7241常用于挤出热空气硫化成型。The silicone rubber is vulcanized by organic peroxide for manufacturing cold shrinkable electric cable accessories,TRK7141 and TRk7341 are cured by heating compression molding; TRK7241 is extruded and cured by hot-air.

微信图片_20240627141749.png

微信图片_20240627141746.png

微信图片_20240627141744.png

产品特性 Key Features

优越的电绝缘性能

Excellent electric insulating property

高拉伸强度,高伸长率和撕裂强度

High tensile strength, high elongation and tear strength

高回弹率，低定伸变形

High rebound rate and low tension set

优良的耐漏电起痕性能

Excellent tracking resistance

良好的耐紫外线，耐臭氧，耐候性

Good ultraviolet resistance, ozone resistance and weather resistance

主要应用 Applications

中、低、高压绝缘材料，冷缩电力电缆附件（终端、中间接头、套管）和避雷器等。

Medium/low/high voltage resistant insulating material, cold shrinkable electric cable accessories ( terminals, connectors, bushing) and lightning arrester etc.

包装 Packaging: 20千克/箱（20Kg/box）

典型物理性能 Typical properties

物性	测试方法	单位	TRK7141	TRK7341	TRK7241
外观			乳白色milky	乳白色milky	半透明translucent
邵氏硬度hardness	D2204	Shore A	40	40	40
拉伸强度Tensile Strength	D412	MPa	9.5	9.2	10.0
断裂伸长率Elongation at break	D412	%	760	720	780
撕裂强度Tear Strength	D624B	KN/m	30	30	35
定伸变形tension set keeping 300% extension for 8hrs at 175℃	D412	%	8.0	8.0	8.0
体积电阻率Volume resistivity	IEC60093	Ωcm	2x10*15	1.5x10*15	3x10*15
介电强度Dielectric strength	IEC60243	KV/mm	26	26	26
耐漏电起痕性Tracking resistance	IEC60587	Grade	户内用	1A4.5 户外用	--
介电常数50HZ Dielectric constant	IEC60250		2.8	2.8	2.8
介电损耗因数50HZ Dissipation factor	IEC60250		0.0017	0.0018	0.0015
硫化剂种类Type of Vulcanization agent			DBPH		DCBP
硫化条件Vulcanizing conditions			170℃x10mins +200℃x4hrs		120℃x10mins +200℃x4hrs

以上数据仅供参考，具体成型工艺与产品选择请联系我公司。 The data are for reference only，Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture. The shelf life is 24 months.

02/有机过氧化物热硫化制造预制式电缆附件用绝缘固体硅橡胶

Solid insulating silicone rubber vulcanized by organic peroxide to make prefabricated cable accessories

型号 Model：TRK7040, TRK7050

产品描述 Product Description

该类产品是用有机过氧化物热硫化的绝缘固体硅橡胶，适合于模压成型生产预制式电缆附件，其中TRK7040, TRK7050常用于加热模压硫化成型。The silicone rubber compounds are solid insulating silicone rubber vulcanized by organic peroxide for making prefabricated cable accessories by high temperature vulcanization and compression -molding.

产品特性 Key Features

优越的电绝缘性能

Excellent electric insulating properties

很好的力学性能

Good mechanical properties

高回弹率，低定伸变形

Hhigh rebound rate and low tension set

良好的耐紫外线，耐臭氧，耐候性

Good ultraviolet resistance, ozoneresistance and weather resistance

主要应用 Applications

生产预制式电缆附件等 To make prefabricated cable accessories

包装 Packaging: 20千克/箱（20Kg/box）

典型物理性能 Typical properties

物性	测试方法	单位	TRK7040	TRK7050
外观			半透明translucent	半透明translucent
邵氏硬度hardness	D2204	Shore A	40	50
拉伸强度Tensile Strength	D412	MPa	9.0	9.2
断裂伸长率Elongation at break	D412	%	600	550
撕裂强度Tear Strength	D624B	KN/m	30	30
扯断永久变形Tensile set at break	D412	%	3.0	3.0
体积电阻率Volume resistivity	IEC60093	Ωcm	2x10*15	1.5x10*15
介电强度Dielectric strength	IEC60243	KV/mm	23	23
介电常数50HZ Dielectric constant	IEC60250		2.8	2.8
介电损耗因数50HZ Dissipation factor	IEC60250		0.0017	0.0018
硫化剂种类Type of Vulcanization agent			DBPH
硫化条件Vulcanizing conditions			170℃x10mins +200℃x4hrs

以上数据仅供参考，具体成型工艺与产品选择请联系我公司。The data are for reference only. Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture，The shelf life is 24 months.

03/有机过氧化物热硫化制造电气防护盒用绝缘固体硅橡胶

Solid insulating HTV silicone rubber vulcanized by organic peroxide to make electric enclosure

型号 Model：TRK1143, TRK1153, TRK1163

产品描述 Product Description

该类产品是用有机过氧化物热硫化的绝缘固体硅橡胶，适合于模压成型生产。

The silicone rubber compounds are solid insulating HTV silicone rubber vulcanized by organic peroxide for making electric enclosure and used for compression-molding.

产品特性 Key Features

良好的电绝缘性能

Good electric insulating properties

良好的力学性能

Good mechanical properties

良好的耐紫外线，耐臭氧，耐候性

Good ultraviolet resistance, ozone resistance and weather resistance

主要应用 Applications

用于生产电气防护盒等 To make electric enclosure

包装 Packaging: 20千克/箱（20Kg/box）

典型物理性能 Typical properties

物性	测试方法	单位	TR1143	TRK1153	TRK1163
外观			半透明translucent	半透明translucent	半透明translucent
比重specific gravity	D792	g/cm*3	1.13	1.16	1.20
邵氏硬度hardness	D2204	Shore A	40	50	60
拉伸强度Tensile Strength	D412	MPa	8	8	7.5
断裂伸长率Elongation at break	D412	%	650	550	500
撕裂强度Tear Strength	D624B	KN/m	24	26	26
体积电阻率Volume resistivity	IEC60093	Ωcm	2x10*14	1.5x10*14	3 x10*14
介电强度Dielectric strength	IEC60243	KV/mm	20	20	20
介电常数50HZ Dielectric constant	IEC60250		2.8	2.9	2.9
介电损耗因数50HZ Dissipation factor	IEC60250		0.01	0.01	0.01
硫化剂种类Type of Vulcanization agent			DBPH-2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane
硫化条件Vulcanizing conditions			170℃x10mins +200℃x4hrs

以上数据仅供参考,具体成型工艺与产品选择请联系我公司。The data are for reference only. Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture，The shelf life is 24 months.

04/有机过氧化物热硫化生产绝缘子用固体硅橡胶

Organic peroxide vulcanization solid silicone rubber to make insulator

型号 Model：TRK7860, TRK7870, TRK7960, TRK7970

产品描述 Product Description

该系列产品是用有机过氧化物热硫化的绝缘固体硅橡胶，适合生产高压绝缘子和避雷器，常用于加热模压硫化成型。

The silicone rubber compounds are vulcanized by organic peroxide for manufacturing high voltage insulator and lightning arrester，The products are cured by heating compression molding.

产品特性 Key Features

优越的电绝缘性能

Excellent electric insulating property

优良的耐漏电起痕性能

Excellent tracking resistance

良好的耐冷热老化稳定性

Excellent thermal-aging and cold-brittle stability

良好的耐紫外线，耐臭氧，耐候性

Good ultraviolet resistance, ozone resistance and weather resistance

主要应用 Applications

用于生产中高压绝缘子和避雷器等

The products should be used for making Medium and high voltage resistant insulator and lightning arrester etc.

微信图片_20240627141751.png

包装 Packaging: 20千克/箱（20Kg/box）

典型物理性能 Typical properties

物性	测试方法	单位	TRK7860	TRK7870	TRK7960	TRK7970
外观			浅灰色，深红色
邵氏硬度hardness	D2204	Shore A	60	69	60	70
拉伸强度Tensile Strength	D412	MPa	5.0	5.0	5.5	5.5
断裂伸长率Elongation at break	D412	%	250	250	300	280
撕裂强度Tear Strength	D624B	KN/m	12	12	14	14
扯断永久变形Tensile set at break	D412	%	3.0	3.0	3.0	3.0
体积电阻率Volume resistivity	IEC60093	Ωcm	2x10*15	1.5x10*15	3x10*15	3x10*15
介电强度Dielectric strength	IEC60243	KV/mm	22	22	24	24
耐漏电起痕性Tracking resistance	IEC60587	Grade	1A4.5	1A4.5	1A4.5	1A4.5
介电常数50HZ Dielectric constant	IEC60250		3.3	3.3	3.3	3.3
介电损耗因数50HZ Dissipation factor	IEC60250		0.005	0.005	0.004	0.004
阻燃性Flammability	UL94V		UL94V-0	UL94V-0	UL94V-0	UL94V-0
硫化条件Vulcanizing conditions			DBPH 170℃x10mins +200℃x4hrs

以上数据仅供参考，具体成型工艺与产品选择请联系我公司。The data are for reference only. Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture. The shelf life is 24 months.

05/有机过氧化物热硫化导电固体硅橡胶

Organic peroxide vulcanization electrically conductive solid silicone rubber

型号 Model：TRK645, TRK651, TRK661

产品描述 Product Description

该系列产品是用有机过氧化物热硫化的导电固体硅橡胶，适合生产冷缩电力电缆附件，常用于加热模压硫化成型。

The silicone rubber compounds are vulcanized by organic peroxide for manufacturing cold shrinkable electric cable accessories。The products are cured by heating compression molding.

产品特性 Key Features

优越的导电性能

Excellent electric conductivity

良好拉伸强度和撕裂强度

Good tensile strength, and tear strength

良好的耐冷热老化稳定性

Excellent thermal-aging and cold-brittle stability

良好的耐紫外线，耐臭氧，耐候性

Good ultraviolet resistance, ozone resistance and weather resistance

主要应用 Applications

用于生产冷缩电力电缆附件（电力终端应力锥、中间接头）等

Used for manufacturing the cold shrinkable electric cable accessories (stress cone terminals, connectors) etc.

包装 Packaging: 20千克/箱（20Kg/box）

典型物理性能 Typical properties

物性	测试方法	单位	TRK645	TRK651	TRK661
外观			黑色 Black
邵氏硬度hardness	D2204	Shore A	40	50	60
拉伸强度Tensile Strength	D412	MPa	6.2	5.5	5.5
断裂伸长率Elongation at break	D412	%	800	600	500
撕裂强度Tear Strength	D624B	KN/m	23	19	20
扯断永久变形Tensile set at break	D412	%	3.0	5.0	5.0
体积电阻率Volume resistivity	IEC60093	Ωcm	87	50	40
硫化剂种类Type of Vulcanization agent			DBPH-2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane
硫化条件Vulcanizing conditions			170℃x10mins +200℃x4hrs

以上数据仅供参考，具体成型工艺与产品选择请联系我公司。The data are for reference only. Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture. The shelf life is 24 months.

06/加成型双组分铂金硫化剂热硫化绝缘固体硅橡胶

Insulating solid silicone rubber cured by addition reaction two-part A/B curing agent

型号 Model：RK7235P, TRK7241P

产品描述 Product Description

该系列产品是用加成型双组分铂金硫化剂热硫化的绝缘固体硅橡胶，适合生产冷缩电力套管电缆附件常用于挤出热空气硫化成型。

The silicone rubber compounds are vulcanized by addition reaction two-part A/B curing agent for manufacturing cold shrinkable tubing etc. electric cable accessories , is extruded and cured by hot-air.

产品特性 Key Features

优越的电绝缘性能

Excellent electric insulating property

高拉伸强度,高伸长率和撕裂强度

High tensile strength, high elongation and tear strength

高回弹率，低定伸变形

High rebound rate and low tension set

良好的耐冷热老化稳定性

Excellent thermal-aging and cold-brittle stability(-60—250℃)

良好的耐紫外线，耐臭氧，耐候性

Good ultraviolet resistance, ozone resistance and weather resistance

主要应用 Applications

生产冷缩电力套管等电缆附件/通讯冷缩管/母排管

The product is manufactured the cold shrinkable electric cable accessories ， cold shrinkable tubing in telecommunication field and bus duct.

包装 Packaging: 20千克/箱（20Kg/box）

典型物理性能 Typical properties

物性	测试方法	单位	TRK7235P	TRK7241P	TRK7251P	TRK7261P
外观			半透明translucent
邵氏硬度hardness	D2204	Shore A	37	40	52	63
拉伸强度Tensile Strength	D412	MPa	9.5	9.8	9.5	10
断裂伸长率Elongation at break	D412	%	760	720	660	450
撕裂强度Tear Strength	D624B	KN/m	30	30	32	35
扯断永久变形Tensile set at break	D412	%	3.0	3.0	3.0	3.0
定伸变形tension set keeping 300% extension for 8hrs at 175℃	D412	%	8.0冷缩管	8.0冷缩管	--母排管	--母排管
体积电阻率Volume resistivity	IEC60093	Ωcm	8x10*15	8x10*15	8x10*15	8x10*15
介电强度Dielectric strength	IEC60243	KV/mm	25	25	25	25
介电常数50HZ Dielectric constant	IEC60250		2.8	2.8	2.9	2.9
介电损耗因数50HZ Dissipation factor	IEC60250		0.0017	0.0018	0.003	0.003
硫化剂种类Type of Vulcanization agent			A agent (Pt), B agent (cross-linking agent and inhibitor)
硫化条件Vulcanizing conditions			130℃x5mins+200℃x4hrs

以上数据仅供参考，具体成型工艺与产品选择请联系我公司。The data are for reference only. Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture. The shelf life is 24 months.

07/双组分绝缘液体硅橡胶LIMS

Two-part A/B insulating liquid silicone rubber

型号 Model：LSR7316-35A/B, LSR7316-40A/B, LSR7216-40A/B

产品描述 Product Description

该类产品是双组份绝缘液体硅橡胶，用于液体注射成型生产电缆附件。

The silicone rubber compounds are two-part A/B insulating liquid silicone rubber, used for liquid injection molding system to manufacture cable accessories.

产品特性 Key Features

优越的电绝缘性能

Excellent electric insulating property

高拉伸强度,高伸长率和撕裂强度

High tensile strength, high elongation and tear strength

高回弹率，低定伸变形

High rebound rate and low tension set

优良的耐漏电起痕性能

Excellent tracking resistance

良好的耐紫外线，耐臭氧，耐候性

Good ultraviolet resistance, ozone resistance and weather resistance

主要应用 Applications:

LSR7316-35A/B, LSR7316-40A/B 适合生产中低压电力电缆附件（冷缩管、户内/户外终端、可分离式电缆连接头，中间头等），LSR7216-40A/B适合生产高压66KV,110KV中间头和终端等电缆附件。

LSR7316-35A/B, LSR7316-40A/B are used for liquid injection molding system to manufacture medium /low voltage resistant electric cable accessories ( cold shrinkable tubing，indoor/outdoor terminals, connectors etc).LSR7216-40A/B is used for liquid injection molding system to manufacture high voltage resistant electric cable accessories such as 66KV, 110KV terminals, connectors etc)

包装 Packaging: 200千克/桶（200Kg/drum）

典型物理性能 Typical properties

物性	测试方法	单位	TRK7316-35A/B	TRK7316-40A/B	TRK7216-40A/B
外观			A/B:透明/灰色 transparent/grey	A/B：透明transparent	A/B：透明transparent
固体含量 solid content		%	100	100	100
粘度Viscosity(Y=1.0 min-1)		Pa S	1500/1600	1500/1600	800/900
硫化速度T10/T90(130℃)		S	30/50	30/50	25/45
比重specific gravity	D792	g/cm*3	1.13	113	1.10
邵氏硬度hardness	D2204	Shore A	38	43	40
拉伸强度Tensile Strength	D412	MPa	9.5	10	8.5
断裂伸长率Elongation at break	D412	%	720	780	580
撕裂强度Tear Strength	D624B	KN/m	30	30	28
扯断永久变形Tensile set at break	D412	%	3.0	3.0	3.0
定伸变形tension set keeping 300% extension for 8hrs at 175℃	D412	%	8.0	8.0	8.0
体积电阻率Volume resistivity	IEC60093	Ωcm	2x10*16	1.5x10*16	3x10*16
介电强度Dielectric strength	IEC60243	KV/mm	26	26	26
耐漏电起痕性Tracking resistance	IEC60587	Grade	1A4.5	1A4.5	1A4.5
介电常数50HZ Dielectric constant	IEC60250		2.8	2.8	2.8
介电损耗因数50HZ Dissipation factor	IEC60250		0.0015	0.0015	0.0015
硫化条件Vulcanizing conditions			130℃x10mins +200℃x4hrs

以上数据仅供参考，具体成型工艺与产品选择请联系我公司。The data are for reference only. Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture. The shelf life is 24 months.

08/双组分导电液体硅橡胶LIMS

Two-part A/B electrically conductive liquid silicone rubber

型号 Model：LSR7616-40A/B

产品描述 Product Description

该类产品是双组份导电液体硅橡胶，用于液体注射成型生产电缆附件。

The silicone rubber compounds are two-part A/B electrically conductive liquid silicone rubber, used for liquid injection molding system to manufacture cable accessories.

产品特性 Key Features

优越的导电性能

Excellent electric conductivity

高拉伸强度和撕裂强度

High tensile strength and tear strength

低粘度，流动性好

Low viscosity , good fluid

硫化时间稳定（T10/T90）

Stable vulcanizing time

主要应用 Applications:

LSR7616-40A/B 适合生产中/低/高压电力电缆附件（应力锥，中间头等）。

LSR7616-40A/B are used for liquid injection molding system to manufacture medium /low/high voltage resistant electric cable accessories (stress cone terminals, connectors etc).

包装 Packaging: 200千克/桶（200Kg/drum）

典型物理性能 Typical properties

物性	测试方法	单位	TRK7616-40A/B
外观			A/B：黑色black
固体含量 solid content		%	100
粘度Viscosity(Y=1.0 min-1)		Pa S	2000/2200
硫化速度T10/T90(130℃)		S	30/68
比重specific gravity	D792	g/cm*3	1.14
邵氏硬度hardness	D2204	Shore A	40
拉伸强度Tensile Strength	D412	MPa	6.2
断裂伸长率Elongation at break	D412	%	480
撕裂强度Tear Strength	D624B	KN/m	33
体积电阻率Volume resistivity	IEC60093	Ωcm	90
硫化条件Vulcanizing conditions

以上数据仅供参考，具体成型工艺与产品选择请联系我公司. The data are for reference only. Please contact us for details.

备注 Remarks：

产品在室温下密封储存于室内通风干燥处，避免阳光直接照射，储存期为24个月。

The products should be closed tightly and avoided from lighting directly and moisture. The shelf life is 24 months.

关于我们

东莞市同锐凯新材有限公司注册成立于2012年，是一家专业从事固体硅橡胶及液体硅橡胶材料研发、生产与销售的高科技型制造企业，下辖深圳市同锐凯新材料有限公司、东莞市同锐凯新材料有限公司，公司生产基地位于东莞市桥头镇，占地面积2万平方米，年产能过万吨，产品种类包括：气相胶、阻燃胶、耐火胶、耐热胶、耐水蒸汽胶、耐油胶、自析油胶、低压缩永久变形胶、导电胶、抗静电胶、电力绝缘胶、绝缘子生产用胶等，广泛应用于电子电器、电力通讯、交通运输、航空航天、能源水利、工业机械、医疗卫生、日常生活用品等各个领域。

微信图片_20240627141754.png

公司拥有全部产品的自主知识产权，先进的硅橡胶专用生产设备及检测、研发仪器设备，通过精选合格供应商来优选原料、生产过程施行严格的中间控制及成品检验，保证公司产品的优质稳定，可根据客户需求快捷提供个性化解决方案及技术支持。2012年公司通过ISO9001国际质量管理体系认证，产品通过美国UL产品认证、GEMT检测认证、ROHS、REACH、FDA、LFGB等多项SGS权威检测认证。成为客户的战略合作伙伴，与客户、员工共同成长，我公司正以脚踏实地、努力拚搏的精神全力打造自己的品牌，力争为全球客户提供优质、安全、环保的硅橡胶材料，为⺠族工业的发展贡献自己的一份力量!

微信图片_20240627141759.png

微信公众号同步更新资讯

标签：硅橡胶白炭黑单体中间体硅油有机硅硅全球有机硅网

上一篇：盛大开幕！耀发、精日、古田、兴发、安品、密炼、聚力……众多品牌亮相！

下一篇：展商名单公布丨硅宝、陶氏、古田、圣戈班、瓦克、集泰即将亮相ASE CHINA 2024